The physical properties of Gas Phase silicone are obviously superior to Commercial silicone. For example, the surface gloss, transparency, tensile strength, elongation, tear stength. Bright colors, smooth surface, high transparency, excellent resistance to high and low temperature, non-toxic and environmentally friendly, high strength, tear resistance, aging resistance, excellent insulation, flame retardancy, etc.
Transparent(Gas Phase Silicone),Red, etc. Colors and models can be customized according to customers’ demand.
Application:electronic industry, wood industry, electrical industry, automobile industry, chemical industry, light industry, photovoltaic industry, power industry, energy industry, laminating machine, glass industry, food industry, aviation industry, ship industry, printing, oven, vacuum blister, film covering, packaging, machinery and equipment, sealing industry, bag making machine, and so on.
| Original Properties | Commercial Silicone | FDA Grade Silicone | Gas Phase Silicone | Gas Phase FDA Silicone | Flame-resistant Silicone | Anti-Static Silicone |
| Density | 1.25g/cm3 | 1.25g/cm3 | 1.25g/cm3 | 1.25g/cm3 | 1.5g/cm3 | 1.25g/cm3 |
| Hardnese (Shore A) | 20-30shoreA | 20-30shoreA | 20-30shoreA | 20-30shoreA | 20-30shoreA | 20-30shoreA |
| Tensile Strength | 6Mpa≥ | 6Mpa≥ | 8.5Mpa≥ | 8.5Mpa≥ | 5Mpa≥ | 6Mpa≥ |
| Elongation | 300%≥ | 300%≥ | 500%≥ | 500%≥ | 300%≥ | 400%≥ |
| Tensile Set | 10%≤ | 10%≤ | 8%≤ | 8%≤ | ||
| Temperature Range | -40℃-200℃ | -40℃-200℃ | -40℃-200℃ | -40℃-200℃ | -40℃-260℃ | -40℃-200℃ |
| Tear Strength | 18KN/m≥ | 20KN/m≥ | 30KN/m≥ | 32KN/m≥ | ||
| Food Safety | General Industry Grade | FDA Food Grade | General Industry Grade | FDA食品级 | General Industry Grade | General Industry Grade |
| Odor Test | Slight vulcanizing agent smell | Almost tasteless | Slight vulcanizing agent smell | Amost tasteless | Slight vulcanizing agent smell | Slight vulcanizing agent smell |
| Flame Resistance | FV-1 | FV-1 | FV-1 | FV-1 |